Brazing alloys, soft solders and preforms

Brazing alloys

When it comes to joining different or identical materials such as stainless steel, aluminum, non-ferrous metals (brass alloys, etc.) firmly and bonded, H.P. Wirth is your reliable supplier for brazing alloys. We work with long-standing partners to ensure consistent quality at the highest level. We are glad to use the material provided if required. Special geometries or special profiles for your individual requirements are manufactured in our own semi-finished product department.

.

In manufacturing possibilities, you find an extract from our product range or rather from the possible geometric shape which we can produce for you. Our potential in this field is almost unlimited and in accordance with our slogan WE CREATE SOLUTIONS we produce for your application the proper brazing preforms as well.

Flux-filled aluminum alloy

If your process requires the use of flux, we can provide it for you. Nevertheless, there is the possibility, especially in the area of ​​aluminum molded parts, to fabricate them from material filled with flux or finally to coat the component with flux.

Feel free to contact us – we will take care of your solution.

Aluminum alloys

If necessary, we will also use the material you have provided. In manufacturing possibilities, you find an extract from our product range as well as the possible geometric shapes.

If flux is required, we can produce aluminum alloys from flux-filled material or finally coat the component with flux.

TitleDin En Iso 17672Abbreviation Din En 1044En Iso 3677 1995Din 8513
HPW-103AlAl 110AL 103B-Al90Si-575/590-
HPW-104AlAl 112AL 104B-Al88Si-575/585-

Copper-, brass- and nickel silver alloys

Depending on the customers’ requirements, we can also process the material you make available.

You find an extract from our product range as well as possible geometric shapes in manufacturing possibilities.

TitleDin En Iso 17672Abbreviation Din En 1044En Iso 3677 1995Din 8513
HPW-102CuCu 102, Cu 110, Cu 141CU 102, CU 101, CU 104B-Cu1000-1083Of-Cu
HPW-201CuCu 922CU 201B-Cu94Sn(P)-910/1040CuSn6
HPW-202CuCu 925CU 202B-Cu86Sn(P)-825/990CuSn12
HPW-301CuCu 470aCU 301B-Cu60Zn(Si)-875/895L-CuZn40
HPW-303CuCu 680CU 303B-Cu60Zn(Si)(Mn)-870/900L-CuZn40
HPW-305CuCu 773CU 305B-Cu48ZnNi(Si)-890/920L-CuNi10Zn42
HPW-CuMnNi----

Phosphoric brazing alloys

We are glad to process the material you provide on request.

In manufacturing possibilities, you can inform about our product range as well as possible geometric shapes.

TitleDin En Iso 17672en_iso_3677-1995Din 8513
HPW-101CpCuP 286CP 101-
HPW-102CpCuP 284CP 102L-Ag15P
HPW-104CpCuP 281L-Ag5P
HPW-105CpCuP 279L-Ag2P
HPW-201CpCuP 182L-CuP8
HPW-202CpCuP 180L-CuP7
HPW-203CpCuP 179L-CuP6
HPW-302CpCuP 386-

Silver solder

Would you like us to use your own material in production? No problem – feel free to contact us.

Information about our product range as well as possible geometric shapes are provided in manufacturing possibilities.

TitleDin En Iso 17672Abbreviation Din En 1044En Iso 3677 1995Din 8513
HPW-102AgAg 156B-Ag56CuZnSn-620/655L-Ag55Sn
HPW-103AgAg 155B-Ag55ZnCuSn-630/660L-Ag55Sn
HPW-104AgAg 145B-Ag45CuZnSn-640/680L-Ag45Sn
HPW-105AgAg 140B-Ag40CuZnSn-650/710L-Ag40Sn
HPW-106AgAg 134B-Cu36AgZnSn-630/730L-Ag34Sn
HPW-107AgAG 130B-Cu36ZnAgSn-665/755L-Ag30Sn
HPW-108AgAg 125B-Cu40ZnAgSn-680/760L-Ag25Sn
HPW-201Ag-B-Ag63CuZn-690/730-
HPW-202Ag-B-Ag60CuZn-695/730L-Ag60
HPW-203AgAg 244B-Ag44CuZn-675/735L-Ag44
HPW-204AgAg 230B-Cu38ZnAg-680/765L-Ag30
HPW-205AgAg 225B-Cu40ZnAg-700/790L-Ag25
HPW-206AgAg 220B-Cu43ZnAg(Si)-690/810L-Ag20
HPW-207AgAg 212B-Cu48ZnAg(Si)-800/830L-Ag12
HPW-208AgAg 205B-Cu55ZnAg(Si)-820/870L-Ag5
HPW-401AgAG272B-Ag72Cu-780L-Ag72
HPW-401AgZn--L-Ag72Zn
HPW-502AgAg 449-B-Ag49ZnCuMnNi-680/705L-Ag49

Special alloys

We also produce your brazing alloys with the material you have supplied.
Inform yourself about our product range as well as possible geometric shapes in manufacturing possibilities.

TitleDin En Iso 17672Abbreviation Din En 1044En Iso 3677 1995Din 8513
HPW-101PdPd587PD 101B-Ag54PdCu-900/950-
HPW-103AuAu 375AU 103B-Cu62Au-980/1000-
HPW-103PdPd481PD 103B-Ag65CuPd-850/900-
HPW-105AuAu827AU 105B-Au82Ni-950-
HPW-105PdPd387PD 105B-Ag58CuPd-825/850-
HPW-106PdPd287PD 106B-Ag68CuPd-805/810-
HPW-5050AuAu 503-B-Au50Cu-955/970-

Further options to filter:

Didn’t find what you were looking for in our material tables? Maybe a different sorting will help you.

Brazing alloys sorted by technical standards

TitleDin En Iso 17672CompositionWorking Temperaturecategories_hfilter
HPW-101CpCuP 286Cu 73,5 - 76,4% | Ag 17,0 - 19,0% | P 6,6 -7,5%0650 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-101PdPd587Ag 54,0% | Pd 25,0% | Cu 21,0%0955 °Cbrazing-alloys special-brazing-alloys
HPW-102AgAg 156brazing-alloys silver-brazing-alloys
HPW-102CpCuP 284Cu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%0700 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-102CuCu 102, Cu 110, Cu 141Cu 99,9 - 100% | P 0 - 0,075%11120 °Cbrazing-alloys copper-based-brazing-alloys
HPW-103AgAg 155brazing-alloys silver-brazing-alloys
HPW-103AlAl 110Al 87,5- 91,0% | Si 9,0 - 11,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Ti 0 - 0,2% | Zn 0 - 0,1% | Mn 0 - 0,05% | Mg 0 - 0,05% 0595 °Caluminium-based-brazing-alloys brazing-alloys
HPW-103AuAu 375Cu 62,5% | Au 37,5%11000 °Cbrazing-alloys special-brazing-alloys
HPW-103PdPd481Ag 54,0% | Pd 25,0% | Cu 21,0%0905 °Cbrazing-alloys special-brazing-alloys
HPW-104AgAg 145brazing-alloys silver-brazing-alloys
HPW-104AlAl 112Al 85,5 - 89,0% | Si11,0 - 13,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Zn 0 - 0,2% | Mn 0 - 0,15% | Mg 0 - 0,1%0590 °Caluminium-based-brazing-alloys brazing-alloys
HPW-104CpCuP 281brazing-alloys phosphorus-bearing-brazing-alloys
HPW-105AgAg 140brazing-alloys silver-brazing-alloys
HPW-105AuAu827Au 82,0% | Ni 18,0%0950 °Cbrazing-alloys special-brazing-alloys
HPW-105CpCuP 279brazing-alloys phosphorus-bearing-brazing-alloys
HPW-105PdPd387Ag 58,5% | Cu 31,5% | Pd 10,0%0860 °Cbrazing-alloys special-brazing-alloys
HPW-106AgAg 134brazing-alloys silver-brazing-alloys
HPW-106PdPd287Ag 68,4% | Cu 26,6% | Pd 5,0%0815 °Cbrazing-alloys special-brazing-alloys
HPW-107AgAG 130brazing-alloys silver-brazing-alloys
HPW-108AgAg 125brazing-alloys silver-brazing-alloys
HPW-201Ag-brazing-alloys silver-brazing-alloys
HPW-201CpCuP 182brazing-alloys phosphorus-bearing-brazing-alloys
HPW-201CuCu 922Cu 92,6 - 94,5% | Sn 5,5 - 7,0% | P 0,01 - 0,4%11060 °Cbrazing-alloys copper-based-brazing-alloys
HPW-202Ag-brazing-alloys silver-brazing-alloys
HPW-202CpCuP 180brazing-alloys phosphorus-bearing-brazing-alloys
HPW-202CuCu 925Cu 86,6 - 88,9% | Sn 11,0 - 13,0% | P 0,01 - 0,4%11040 °Cbrazing-alloys copper-based-brazing-alloys
HPW-203AgAg 244brazing-alloys silver-brazing-alloys
HPW-203CpCuP 179brazing-alloys phosphorus-bearing-brazing-alloys
HPW-204AgAg 230brazing-alloys silver-brazing-alloys
HPW-205AgAg 225brazing-alloys silver-brazing-alloys
HPW-206AgAg 220brazing-alloys silver-brazing-alloys
HPW-207AgAg 212brazing-alloys silver-brazing-alloys
HPW-208AgAg 205brazing-alloys silver-brazing-alloys
HPW-301CuCu 470aCu 58,5 - 61,5% | Zn 38,1 - 41,3% | Si 0,2 - 0,4%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-302CpCuP 386brazing-alloys phosphorus-bearing-brazing-alloys
HPW-303CuCu 680Cu 56,0 - 60,0% | Zn 36,2 - 42,7% | Sn 0,8 - 1,1% | Fe 0,2 - 1,2% | Ni 0,2 - 0,8% | Si 0,04 - 0,2% | Mn 0,01% - 0,5%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-305CuCu 773Cu 46,0 - 50,0% | Zn 38,8 - 44,8% | Ni 9,0 - 11,0% | Si 0,15 - 0,2%0910 °Cbrazing-alloys copper-based-brazing-alloys
HPW-401AgAG272brazing-alloys silver-brazing-alloys
HPW-401AgZn-brazing-alloys silver-brazing-alloys
HPW-502AgAg 449Ag 48,0 - 50,0% | Zn 21,0 - 25,0% | Cu 15,0 - 17,0% | Mn 7,0 - 8,0% | Ni 4,0 - 5,0%0610 °Csilver-brazing-alloys uncategorized brazing-alloys
HPW-5050AuAu 503Au 50,0% | Cu 50,0%0970 °Cbrazing-alloys special-brazing-alloys
HPW-CuMnNi-Cu 86% | Mn 12% | Ni 2%0990 °Cbrazing-alloys copper-based-brazing-alloys

* zurückgezogen

TitleAbbreviation Din En 1044CompositionWorking Temperaturecategories_hfilter
HPW-101CpCP 101Cu 73,5 - 76,4% | Ag 17,0 - 19,0% | P 6,6 -7,5%0650 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-101PdPD 101Ag 54,0% | Pd 25,0% | Cu 21,0%0955 °Cbrazing-alloys special-brazing-alloys
HPW-102Agbrazing-alloys silver-brazing-alloys
HPW-102CpCP 102Cu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%0700 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-102CuCU 102, CU 101, CU 104Cu 99,9 - 100% | P 0 - 0,075%11120 °Cbrazing-alloys copper-based-brazing-alloys
HPW-103Agbrazing-alloys silver-brazing-alloys
HPW-103AlAL 103Al 87,5- 91,0% | Si 9,0 - 11,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Ti 0 - 0,2% | Zn 0 - 0,1% | Mn 0 - 0,05% | Mg 0 - 0,05% 0595 °Caluminium-based-brazing-alloys brazing-alloys
HPW-103AuAU 103Cu 62,5% | Au 37,5%11000 °Cbrazing-alloys special-brazing-alloys
HPW-103PdPD 103Ag 54,0% | Pd 25,0% | Cu 21,0%0905 °Cbrazing-alloys special-brazing-alloys
HPW-104Agbrazing-alloys silver-brazing-alloys
HPW-104AlAL 104Al 85,5 - 89,0% | Si11,0 - 13,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Zn 0 - 0,2% | Mn 0 - 0,15% | Mg 0 - 0,1%0590 °Caluminium-based-brazing-alloys brazing-alloys
HPW-104Cpbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-105Agbrazing-alloys silver-brazing-alloys
HPW-105AuAU 105Au 82,0% | Ni 18,0%0950 °Cbrazing-alloys special-brazing-alloys
HPW-105Cpbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-105PdPD 105Ag 58,5% | Cu 31,5% | Pd 10,0%0860 °Cbrazing-alloys special-brazing-alloys
HPW-106Agbrazing-alloys silver-brazing-alloys
HPW-106PdPD 106Ag 68,4% | Cu 26,6% | Pd 5,0%0815 °Cbrazing-alloys special-brazing-alloys
HPW-107Agbrazing-alloys silver-brazing-alloys
HPW-108Agbrazing-alloys silver-brazing-alloys
HPW-201Agbrazing-alloys silver-brazing-alloys
HPW-201Cpbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-201CuCU 201Cu 92,6 - 94,5% | Sn 5,5 - 7,0% | P 0,01 - 0,4%11060 °Cbrazing-alloys copper-based-brazing-alloys
HPW-202Agbrazing-alloys silver-brazing-alloys
HPW-202Cpbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-202CuCU 202Cu 86,6 - 88,9% | Sn 11,0 - 13,0% | P 0,01 - 0,4%11040 °Cbrazing-alloys copper-based-brazing-alloys
HPW-203Agbrazing-alloys silver-brazing-alloys
HPW-203Cpbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-204Agbrazing-alloys silver-brazing-alloys
HPW-205Agbrazing-alloys silver-brazing-alloys
HPW-206Agbrazing-alloys silver-brazing-alloys
HPW-207Agbrazing-alloys silver-brazing-alloys
HPW-208Agbrazing-alloys silver-brazing-alloys
HPW-301CuCU 301Cu 58,5 - 61,5% | Zn 38,1 - 41,3% | Si 0,2 - 0,4%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-302Cpbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-303CuCU 303Cu 56,0 - 60,0% | Zn 36,2 - 42,7% | Sn 0,8 - 1,1% | Fe 0,2 - 1,2% | Ni 0,2 - 0,8% | Si 0,04 - 0,2% | Mn 0,01% - 0,5%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-305CuCU 305Cu 46,0 - 50,0% | Zn 38,8 - 44,8% | Ni 9,0 - 11,0% | Si 0,15 - 0,2%0910 °Cbrazing-alloys copper-based-brazing-alloys
HPW-401Agbrazing-alloys silver-brazing-alloys
HPW-401AgZnbrazing-alloys silver-brazing-alloys
HPW-502Ag-Ag 48,0 - 50,0% | Zn 21,0 - 25,0% | Cu 15,0 - 17,0% | Mn 7,0 - 8,0% | Ni 4,0 - 5,0%0610 °Csilver-brazing-alloys uncategorized brazing-alloys
HPW-5050Au-Au 50,0% | Cu 50,0%0970 °Cbrazing-alloys special-brazing-alloys
HPW-CuMnNi-Cu 86% | Mn 12% | Ni 2%0990 °Cbrazing-alloys copper-based-brazing-alloys

TitleEn Iso 3677 1995CompositionWorking Temperaturecategories_hfilter
HPW-101CpB-Cu75AgP-645Cu 73,5 - 76,4% | Ag 17,0 - 19,0% | P 6,6 -7,5%0650 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-101PdB-Ag54PdCu-900/950Ag 54,0% | Pd 25,0% | Cu 21,0%0955 °Cbrazing-alloys special-brazing-alloys
HPW-102AgB-Ag56CuZnSn-620/655brazing-alloys silver-brazing-alloys
HPW-102CpB-Cu80AgP-645/800Cu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%0700 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-102CuB-Cu1000-1083Cu 99,9 - 100% | P 0 - 0,075%11120 °Cbrazing-alloys copper-based-brazing-alloys
HPW-103AgB-Ag55ZnCuSn-630/660brazing-alloys silver-brazing-alloys
HPW-103AlB-Al90Si-575/590Al 87,5- 91,0% | Si 9,0 - 11,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Ti 0 - 0,2% | Zn 0 - 0,1% | Mn 0 - 0,05% | Mg 0 - 0,05% 0595 °Caluminium-based-brazing-alloys brazing-alloys
HPW-103AuB-Cu62Au-980/1000Cu 62,5% | Au 37,5%11000 °Cbrazing-alloys special-brazing-alloys
HPW-103PdB-Ag65CuPd-850/900Ag 54,0% | Pd 25,0% | Cu 21,0%0905 °Cbrazing-alloys special-brazing-alloys
HPW-104AgB-Ag45CuZnSn-640/680brazing-alloys silver-brazing-alloys
HPW-104AlB-Al88Si-575/585Al 85,5 - 89,0% | Si11,0 - 13,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Zn 0 - 0,2% | Mn 0 - 0,15% | Mg 0 - 0,1%0590 °Caluminium-based-brazing-alloys brazing-alloys
HPW-104CpB-Cu89PAg-645/815brazing-alloys phosphorus-bearing-brazing-alloys
HPW-105AgB-Ag40CuZnSn-650/710brazing-alloys silver-brazing-alloys
HPW-105AuB-Au82Ni-950Au 82,0% | Ni 18,0%0950 °Cbrazing-alloys special-brazing-alloys
HPW-105CpB-Cu92PAg-645/825brazing-alloys phosphorus-bearing-brazing-alloys
HPW-105PdB-Ag58CuPd-825/850Ag 58,5% | Cu 31,5% | Pd 10,0%0860 °Cbrazing-alloys special-brazing-alloys
HPW-106AgB-Cu36AgZnSn-630/730brazing-alloys silver-brazing-alloys
HPW-106PdB-Ag68CuPd-805/810Ag 68,4% | Cu 26,6% | Pd 5,0%0815 °Cbrazing-alloys special-brazing-alloys
HPW-107AgB-Cu36ZnAgSn-665/755brazing-alloys silver-brazing-alloys
HPW-108AgB-Cu40ZnAgSn-680/760brazing-alloys silver-brazing-alloys
HPW-201AgB-Ag63CuZn-690/730brazing-alloys silver-brazing-alloys
HPW-201CpB-Cu92P-710/770brazing-alloys phosphorus-bearing-brazing-alloys
HPW-201CuB-Cu94Sn(P)-910/1040Cu 92,6 - 94,5% | Sn 5,5 - 7,0% | P 0,01 - 0,4%11060 °Cbrazing-alloys copper-based-brazing-alloys
HPW-202AgB-Ag60CuZn-695/730brazing-alloys silver-brazing-alloys
HPW-202CpB-Cu93P-710/820brazing-alloys phosphorus-bearing-brazing-alloys
HPW-202CuB-Cu86Sn(P)-825/990Cu 86,6 - 88,9% | Sn 11,0 - 13,0% | P 0,01 - 0,4%11040 °Cbrazing-alloys copper-based-brazing-alloys
HPW-203AgB-Ag44CuZn-675/735brazing-alloys silver-brazing-alloys
HPW-203CpB-Cu94P-710/890brazing-alloys phosphorus-bearing-brazing-alloys
HPW-204AgB-Cu38ZnAg-680/765brazing-alloys silver-brazing-alloys
HPW-205AgB-Cu40ZnAg-700/790brazing-alloys silver-brazing-alloys
HPW-206AgB-Cu43ZnAg(Si)-690/810brazing-alloys silver-brazing-alloys
HPW-207AgB-Cu48ZnAg(Si)-800/830brazing-alloys silver-brazing-alloys
HPW-208AgB-Cu55ZnAg(Si)-820/870brazing-alloys silver-brazing-alloys
HPW-301CuB-Cu60Zn(Si)-875/895Cu 58,5 - 61,5% | Zn 38,1 - 41,3% | Si 0,2 - 0,4%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-302CpB-Cu86SnP-650/700brazing-alloys phosphorus-bearing-brazing-alloys
HPW-303CuB-Cu60Zn(Si)(Mn)-870/900Cu 56,0 - 60,0% | Zn 36,2 - 42,7% | Sn 0,8 - 1,1% | Fe 0,2 - 1,2% | Ni 0,2 - 0,8% | Si 0,04 - 0,2% | Mn 0,01% - 0,5%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-305CuB-Cu48ZnNi(Si)-890/920Cu 46,0 - 50,0% | Zn 38,8 - 44,8% | Ni 9,0 - 11,0% | Si 0,15 - 0,2%0910 °Cbrazing-alloys copper-based-brazing-alloys
HPW-401AgB-Ag72Cu-780brazing-alloys silver-brazing-alloys
HPW-401AgZn-brazing-alloys silver-brazing-alloys
HPW-502AgB-Ag49ZnCuMnNi-680/705Ag 48,0 - 50,0% | Zn 21,0 - 25,0% | Cu 15,0 - 17,0% | Mn 7,0 - 8,0% | Ni 4,0 - 5,0%0610 °Csilver-brazing-alloys uncategorized brazing-alloys
HPW-5050AuB-Au50Cu-955/970Au 50,0% | Cu 50,0%0970 °Cbrazing-alloys special-brazing-alloys
HPW-CuMnNi-Cu 86% | Mn 12% | Ni 2%0990 °Cbrazing-alloys copper-based-brazing-alloys

* withdrawn

TitleDin 8513CompositionWorking Temperaturecategories_hfilter
HPW-101Cp-Cu 73,5 - 76,4% | Ag 17,0 - 19,0% | P 6,6 -7,5%0650 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-101Pd-Ag 54,0% | Pd 25,0% | Cu 21,0%0955 °Cbrazing-alloys special-brazing-alloys
HPW-102AgL-Ag55Snbrazing-alloys silver-brazing-alloys
HPW-102CpL-Ag15PCu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%0700 °Cbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-102CuOf-CuCu 99,9 - 100% | P 0 - 0,075%11120 °Cbrazing-alloys copper-based-brazing-alloys
HPW-103AgL-Ag55Snbrazing-alloys silver-brazing-alloys
HPW-103Al-Al 87,5- 91,0% | Si 9,0 - 11,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Ti 0 - 0,2% | Zn 0 - 0,1% | Mn 0 - 0,05% | Mg 0 - 0,05% 0595 °Caluminium-based-brazing-alloys brazing-alloys
HPW-103Au-Cu 62,5% | Au 37,5%11000 °Cbrazing-alloys special-brazing-alloys
HPW-103Pd-Ag 54,0% | Pd 25,0% | Cu 21,0%0905 °Cbrazing-alloys special-brazing-alloys
HPW-104AgL-Ag45Snbrazing-alloys silver-brazing-alloys
HPW-104Al-Al 85,5 - 89,0% | Si11,0 - 13,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Zn 0 - 0,2% | Mn 0 - 0,15% | Mg 0 - 0,1%0590 °Caluminium-based-brazing-alloys brazing-alloys
HPW-104CpL-Ag5Pbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-105AgL-Ag40Snbrazing-alloys silver-brazing-alloys
HPW-105Au-Au 82,0% | Ni 18,0%0950 °Cbrazing-alloys special-brazing-alloys
HPW-105CpL-Ag2Pbrazing-alloys phosphorus-bearing-brazing-alloys
HPW-105Pd-Ag 58,5% | Cu 31,5% | Pd 10,0%0860 °Cbrazing-alloys special-brazing-alloys
HPW-106AgL-Ag34Snbrazing-alloys silver-brazing-alloys
HPW-106Pd-Ag 68,4% | Cu 26,6% | Pd 5,0%0815 °Cbrazing-alloys special-brazing-alloys
HPW-107AgL-Ag30Snbrazing-alloys silver-brazing-alloys
HPW-108AgL-Ag25Snbrazing-alloys silver-brazing-alloys
HPW-201Ag-brazing-alloys silver-brazing-alloys
HPW-201CpL-CuP8brazing-alloys phosphorus-bearing-brazing-alloys
HPW-201CuCuSn6Cu 92,6 - 94,5% | Sn 5,5 - 7,0% | P 0,01 - 0,4%11060 °Cbrazing-alloys copper-based-brazing-alloys
HPW-202AgL-Ag60brazing-alloys silver-brazing-alloys
HPW-202CpL-CuP7brazing-alloys phosphorus-bearing-brazing-alloys
HPW-202CuCuSn12Cu 86,6 - 88,9% | Sn 11,0 - 13,0% | P 0,01 - 0,4%11040 °Cbrazing-alloys copper-based-brazing-alloys
HPW-203AgL-Ag44brazing-alloys silver-brazing-alloys
HPW-203CpL-CuP6brazing-alloys phosphorus-bearing-brazing-alloys
HPW-204AgL-Ag30brazing-alloys silver-brazing-alloys
HPW-205AgL-Ag25brazing-alloys silver-brazing-alloys
HPW-206AgL-Ag20brazing-alloys silver-brazing-alloys
HPW-207AgL-Ag12brazing-alloys silver-brazing-alloys
HPW-208AgL-Ag5brazing-alloys silver-brazing-alloys
HPW-301CuL-CuZn40Cu 58,5 - 61,5% | Zn 38,1 - 41,3% | Si 0,2 - 0,4%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-302Cp-brazing-alloys phosphorus-bearing-brazing-alloys
HPW-303CuL-CuZn40Cu 56,0 - 60,0% | Zn 36,2 - 42,7% | Sn 0,8 - 1,1% | Fe 0,2 - 1,2% | Ni 0,2 - 0,8% | Si 0,04 - 0,2% | Mn 0,01% - 0,5%0900 °Cbrazing-alloys copper-based-brazing-alloys
HPW-305CuL-CuNi10Zn42Cu 46,0 - 50,0% | Zn 38,8 - 44,8% | Ni 9,0 - 11,0% | Si 0,15 - 0,2%0910 °Cbrazing-alloys copper-based-brazing-alloys
HPW-401AgL-Ag72brazing-alloys silver-brazing-alloys
HPW-401AgZnL-Ag72Znbrazing-alloys silver-brazing-alloys
HPW-502AgL-Ag49Ag 48,0 - 50,0% | Zn 21,0 - 25,0% | Cu 15,0 - 17,0% | Mn 7,0 - 8,0% | Ni 4,0 - 5,0%0610 °Csilver-brazing-alloys uncategorized brazing-alloys
HPW-5050Au-Au 50,0% | Cu 50,0%0970 °Cbrazing-alloys special-brazing-alloys
HPW-CuMnNi-Cu 86% | Mn 12% | Ni 2%0990 °Cbrazing-alloys copper-based-brazing-alloys

Brazing alloys sorted by application

TitleTagsCompositionWorking Temperaturetags_hfilter
HPW-101CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Heat-resistant up to 200°C, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassCu 73,5 - 76,4% | Ag 17,0 - 19,0% | P 6,6 -7,5%0650 °Cbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux heat-resistant-up-to-200c iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-101PdCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 54,0% | Pd 25,0% | Cu 21,0%0955 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-102AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-102CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassCu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%0700 °Cbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-102CuChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 99,9 - 100% | P 0 - 0,075%11120 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing
HPW-103AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-103AlAluminiumAl 87,5- 91,0% | Si 9,0 - 11,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Ti 0 - 0,2% | Zn 0 - 0,1% | Mn 0 - 0,05% | Mg 0 - 0,05% 0595 °Caluminium-en
HPW-103AuCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsCu 62,5% | Au 37,5%11000 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-103PdCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 54,0% | Pd 25,0% | Cu 21,0%0905 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-104AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-104AlAluminiumAl 85,5 - 89,0% | Si11,0 - 13,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Zn 0 - 0,2% | Mn 0 - 0,15% | Mg 0 - 0,1%0590 °Caluminium-en
HPW-104CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-105AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-105AuCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAu 82,0% | Ni 18,0%0950 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-105CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-105PdCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 58,5% | Cu 31,5% | Pd 10,0%0860 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-106AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-106PdCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 68,4% | Cu 26,6% | Pd 5,0%0815 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-107AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-108AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-201AgSilver, Silver alloyssilver silver-alloys
HPW-201CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-201CuChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 92,6 - 94,5% | Sn 5,5 - 7,0% | P 0,01 - 0,4%11060 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing
HPW-202AgSilver, Silver alloyssilver silver-alloys
HPW-202CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-202CuChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 86,6 - 88,9% | Sn 11,0 - 13,0% | P 0,01 - 0,4%11040 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing
HPW-203AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-203CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-204AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-205AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-206AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-207AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-208AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steelcopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux malleable-cast-iron nickel-base-alloys steel
HPW-301CuChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 58,5 - 61,5% | Zn 38,1 - 41,3% | Si 0,2 - 0,4%0900 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing
HPW-302CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassbrass copper-tin-alloys-together-with-flux-not-suitable-on-sulphur-containing-media for-joining-copper-to-copper-without-flux iron-and-nickel-alloys-heat-resistant-up-to-200c red-brass
HPW-303CuChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 56,0 - 60,0% | Zn 36,2 - 42,7% | Sn 0,8 - 1,1% | Fe 0,2 - 1,2% | Ni 0,2 - 0,8% | Si 0,04 - 0,2% | Mn 0,01% - 0,5%0900 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing
HPW-305CuChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 46,0 - 50,0% | Zn 38,8 - 44,8% | Ni 9,0 - 11,0% | Si 0,15 - 0,2%0910 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing
HPW-401AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, Steelscopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-401AgZnCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, Steelscopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-502AgCopper, Copper alloys Nickel, Heat resistant up to 200° C, Malleable cast iron, Nickel alloys, Precious metal, SteelAg 48,0 - 50,0% | Zn 21,0 - 25,0% | Cu 15,0 - 17,0% | Mn 7,0 - 8,0% | Ni 4,0 - 5,0%0610 °Ccopper copper-alloys-nickel heat-resistant-up-to-200-c malleable-cast-iron nickel-alloys precious-metal steel
HPW-5050AuCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAu 50,0% | Cu 50,0%0970 °Ccopper copper-alloys heat-resistant-up-to-200c joining-copper-to-copper-without-flux nickel-base-alloys precious-metal steels
HPW-CuMnNiChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 86% | Mn 12% | Ni 2%0990 °Cchromium chromium-nickel-steels joining-copper-to-copper-without-flux nickel-base-alloys protective-atmosphere-brazing steels vacuum-brazing

Brazing alloys sorted by working temperature

TitleWorking TemperatureTagsCompositiontaxonomy_hfilter
HPW-101Cp0650 °CBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Heat-resistant up to 200°C, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassCu 73,5 - 76,4% | Ag 17,0 - 19,0% | P 6,6 -7,5%600-700-c-en
HPW-101Pd0955 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 54,0% | Pd 25,0% | Cu 21,0%800-1100-c-en
HPW-102AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel600-700-c-en
HPW-102Cp0700 °CBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brassCu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%600-700-c-en 700-800-c-en
HPW-102Cu11120 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 99,9 - 100% | P 0 - 0,075%ueber-1100-c-en
HPW-103AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel600-700-c-en
HPW-103Al0595 °CAluminiumAl 87,5- 91,0% | Si 9,0 - 11,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Ti 0 - 0,2% | Zn 0 - 0,1% | Mn 0 - 0,05% | Mg 0 - 0,05% 500-600-c-en
HPW-103Au11000 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsCu 62,5% | Au 37,5%800-1100-c-en
HPW-103Pd0905 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 54,0% | Pd 25,0% | Cu 21,0%800-1100-c-en
HPW-104AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel600-700-c-en
HPW-104Al0590 °CAluminiumAl 85,5 - 89,0% | Si11,0 - 13,0% | Fe 0 - 0,8% | Cu 0 - 0,3% | Zn 0 - 0,2% | Mn 0 - 0,15% | Mg 0 - 0,1%500-600-c-en
HPW-104CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brass700-800-c-en
HPW-105AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel600-700-c-en
HPW-105Au0950 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAu 82,0% | Ni 18,0%800-1100-c-en
HPW-105CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brass700-800-c-en
HPW-105Pd0860 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 58,5% | Cu 31,5% | Pd 10,0%800-1100-c-en
HPW-106AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel700-800-c-en
HPW-106Pd0815 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAg 68,4% | Cu 26,6% | Pd 5,0%800-1100-c-en
HPW-107AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel700-800-c-en
HPW-108AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel700-800-c-en
HPW-201AgSilver, Silver alloys700-800-c-en
HPW-201CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brass700-800-c-en
HPW-201Cu11060 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 92,6 - 94,5% | Sn 5,5 - 7,0% | P 0,01 - 0,4%800-1100-c-en
HPW-202AgSilver, Silver alloys700-800-c-en
HPW-202CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brass700-800-c-en
HPW-202Cu11040 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 86,6 - 88,9% | Sn 11,0 - 13,0% | P 0,01 - 0,4%800-1100-c-en
HPW-203AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel700-800-c-en
HPW-203CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brass700-800-c-en
HPW-204AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel700-800-c-en
HPW-205AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel700-800-c-en
HPW-206AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel800-1100-c-en
HPW-207AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel800-1100-c-en
HPW-208AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Malleable cast iron, Nickel-base alloys, Steel800-1100-c-en
HPW-301Cu0900 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 58,5 - 61,5% | Zn 38,1 - 41,3% | Si 0,2 - 0,4%800-1100-c-en
HPW-302CpBrass, Copper-tin-alloys together with flux. Not suitable on sulphur-containing media, For joining copper to copper without flux, Iron- and Nickel alloys. Heat-resistant up to 200°C, Red brass600-700-c-en 700-800-c-en
HPW-303Cu0900 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 56,0 - 60,0% | Zn 36,2 - 42,7% | Sn 0,8 - 1,1% | Fe 0,2 - 1,2% | Ni 0,2 - 0,8% | Si 0,04 - 0,2% | Mn 0,01% - 0,5%800-1100-c-en
HPW-305Cu0910 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 46,0 - 50,0% | Zn 38,8 - 44,8% | Ni 9,0 - 11,0% | Si 0,15 - 0,2%800-1100-c-en
HPW-401AgCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, Steels700-800-c-en
HPW-401AgZnCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, Steels700-800-c-en
HPW-502Ag0610 °CCopper, Copper alloys Nickel, Heat resistant up to 200° C, Malleable cast iron, Nickel alloys, Precious metal, SteelAg 48,0 - 50,0% | Zn 21,0 - 25,0% | Cu 15,0 - 17,0% | Mn 7,0 - 8,0% | Ni 4,0 - 5,0%600-700-c-en
HPW-5050Au0970 °CCopper, Copper alloys, Heat-resistant up to 200°C, Joining copper to copper without flux, Nickel-base alloys, Precious metal, SteelsAu 50,0% | Cu 50,0%800-1100-c-en
HPW-CuMnNi0990 °CChromium, Chromium-nickel steels, Joining copper to copper without flux, Nickel-base alloys, Protective atmosphere brazing, Steels, Vacuum brazingCu 86% | Mn 12% | Ni 2%800-1100-c-en