HPW designation:
HPW-102Ag
Abbreviation DIN EN 1044:
AG 102
DIN 8513
L-Ag55Sn
DIN EN ISO 17672
Ag 156
EN ISO 3677: 1995
B-Ag56CuZnSn-620/655
Composition (mass fraction in%):
Ag 55,0 - 57,0% | Cu 21,0 - 23,0% | Zn 15,0 - 17,0% | Sn 4,5 -5,5%
Working temperature ° C:
0650 °C
Temperature ° C:
Solidus 620 °C, Liquidus 655 °C
Tensile strength of the soldering [N/mm²]
400
density[g/cm³] :
9,5
application