HPW designation:
HPW-203Ag
Abbreviation DIN EN 1044:
AG 203
DIN 8513
L-Ag44
DIN EN ISO 17672
Ag 244
EN ISO 3677: 1995
B-Ag44CuZn-675/735
Composition (mass fraction in%):
Ag 43,0 - 45,0% | Cu 29,0 - 31,0% | Zn 24,0 - 28,0%
Working temperature ° C:
0730 °C
Temperature ° C:
Solidus 675 °C, Liquidus 735 °C
Tensile strength of the soldering [N/mm²]
450
density[g/cm³] :
9,1