HPW designation:
HPW-206Ag
Abbreviation DIN EN 1044:
AG 206
DIN 8513
L-Ag20
DIN EN ISO 17672
Ag 220
EN ISO 3677: 1995
B-Cu43ZnAg(Si)-690/810
Composition (mass fraction in%):
Cu 43,0 - 45,0% | Zn 34,0 - 38,0% | Ag 19,0 - 21,0% | Si 0,05 - 0,25%
Working temperature ° C:
0810 °C
Temperature ° C:
Solidus 690 °C, Liquidus 810 °C
Tensile strength of the soldering [N/mm²]
400
density[g/cm³] :
8,7
application