HPW designation:
HPW-202Ag
Abbreviation DIN EN 1044:
AG 202
DIN 8513
L-Ag60
DIN EN ISO 17672
-
EN ISO 3677: 1995
B-Ag60CuZn-695/730
Composition (mass fraction in%):
Ag 60,0% | Cu 26,0% | Zn 14,0%
Working temperature ° C:
0710 °C
Temperature ° C:
Solidus 695 °C, Liquidus 730 °C
Tensile strength of the soldering [N/mm²]
450
density[g/cm³] :
9,5