HPW designation:
HPW-205Ag
Abbreviation DIN EN 1044:
AG 205
DIN 8513
L-Ag25
DIN EN ISO 17672
Ag 225
EN ISO 3677: 1995
B-Cu40ZnAg-700/790
Composition (mass fraction in%):
Cu 39,0 - 41,0% | Zn 33,0 - 37,0% | Ag 24,0 - 26,0%
Working temperature ° C:
0780 °C
Temperature ° C:
Solidus 700 °C, Liquidus 790 °C
Tensile strength of the soldering [N/mm²]
400
density[g/cm³] :
8,8
application