HPW designation:

HPW-102Cp

Abbreviation DIN EN 1044:

CP 102

DIN 8513

L-Ag15P

DIN EN ISO 17672

CuP 284

EN ISO 3677: 1995

B-Cu80AgP-645/800

Composition (mass fraction in%):

Cu 79,3 - 80,7% | Ag 14,5 - 15,5% | P 4,8 - 5,2%

Working temperature ° C:

0700 °C

Temperature ° C:

Solidus 645 °C, Liquidus 800 °C

Tensile strength of the soldering [N/mm²]

250

Density[g/cm³] :

8,4

Application:

Copper on copper without flux, red brass, brass and copper-tin-alloys with flux. Not to use with sulfate media, iron- and nickel alloys, heat-resisting up to 200°C