HPW designation:
HPW-204Ag
Abbreviation DIN EN 1044:
AG 204
DIN 8513
L-Ag30
DIN EN ISO 17672
Ag 230
EN ISO 3677: 1995
B-Cu38ZnAg-680/765
Composition (mass fraction in%):
Cu 37,0 - 39,0% | Zn 30,0 - 34,0% | Ag 29,0 - 31,0%
Working temperature ° C:
0765 °C
Temperature ° C:
Solidus 680 °C, Liquidus 765 °C
Tensile strength of the soldering [N/mm²]
450
density[g/cm³] :
8,9
application