HPW designation:
HPW-207Ag
Abbreviation DIN EN 1044:
AG 207
DIN 8513
L-Ag12
DIN EN ISO 17672
Ag 212
EN ISO 3677: 1995
B-Cu48ZnAg(Si)-800/830
Composition (mass fraction in%):
Cu 47,0 - 49,0% | Zn 38,0 - 42,0% | Ag 11,0 - 13,0% | Si 0,05 - 0,25%
Working temperature ° C:
0830 °C
Temperature ° C:
Solidus 800 °C, Liquidus 830 °C
Tensile strength of the soldering [N/mm²]
400
density[g/cm³] :
8,5
application