HPW designation:
HPW-201Cp
Abbreviation DIN EN 1044:
CP 201
DIN 8513
L-CuP8
DIN EN ISO 17672
CuP 182
EN ISO 3677: 1995
B-Cu92P-710/770
Composition (mass fraction in%):
Cu 91,9 - 92,5% | P 7,5 - 8,1%
Working temperature ° C:
0720 °C
Temperature ° C:
Solidus 710 °C, Liquidus 770 °C
Tensile strength of the soldering [N/mm²]
250
density[g/cm³] :
8,0
application